Сountry of origin | Great Britain |
---|---|
Brand | Hylomar |
Use | Toughened, two component acrylic adhesive designed for bonding a wide range of substrates |
Product Sizes | 490 ml |
Mix ratio | 10:1 |
Cured tensile strength | 16 N/mm² |
Colour | See in technical properties |
HYLO®BOND M5101 is a toughened, two component acrylic adhesive designed for bonding a wide range of substrates.
This structural methacrylate adhesive has superior peel, shear and compressive properties. HYLO®BOND 5101 displays high toughness and can be used on gaps up to 15mm. it has a gel time of approximately 5 minutes. The adhesive has excellent fatigue and weathering resistance.
Instructions for use
The surface to be bonded can have a great impact on the cured properties of Hylobond. Care must be taken to ensure that all traces of oil, grease and dirt are removed from the substrate. This can be done with a degreasing agent or solvent such as acetone. Abrading or etching the surface can greatly improve the properties of the bonded joint, if this is done a second degreasing process is highly recommended.
Prior to dispensing it is important to extrude the product onto a non-bonding surface to ensure that bead coming out of the nozzle is a uniform grey colour. As soon as the bead is the correct colour the product should be used immediately to prevent curing in the nozzle. Enough adhesive should be used to fill the bond gap before the parts are joined. Once the substrates are joined sufficient pressure should be applied (e.g. by clamping) to avoid dry bonding and prevent movement in the joint. These processes must be completed before the geltime expires.
The optimal application temperature is about 20°C, the geltime and cure time will be affected at temperatures much higher or lower than this. The viscosity is also affected by temperature so to ensure a consistent extrusion rate and geltime the temperature should be kept constant.
Typical Physical Properties
Uncured Materials
Mixing Ratio (By Weight) | Mixing Ratio (By Volume) | Specific Gravity (gml-1) |
Viscosity (@22°C) [cPs] |
Colour |
---|---|---|---|---|
Adhesive |
||||
9 | 10 |
0.97 – 1.01 |
90.000 – 130.000 |
Cream |
Activator |
||||
1 |
1 |
1.04 – 1.14 |
75.000 – 110.000 |
Black |
Mixed Materials
Geltime (@22°C) [min] |
Cure Time (@22°C) [min] |
Gap Filling [ММ] |
Colour |
---|---|---|---|
≈5 |
14 – 18 |
≤15 |
Grey |
Cured Materials
Tensile Strength [Nmm-²] |
Elongation |
Shear Strength PVC/ABS [Nmm-²] |
Shear Strength (Aluminium) [Nmm-²] |
Shear Strength (Aluminium) [Nmm-²] |
Shear Strength (Stainless Steel/Acrylic) [Nmm-²] |
---|---|---|---|---|---|
16 |
75% |
15 |
23 |
18 |
22 |
Documentation
-
Hylo®Bond M5101 - TDS.pdf
168.45 Kb -
Hylo®Bond M5101 Activator - American MSDS.pdf
261.83 Kb -
Hylo®Bond M5101 Activator - English MSDS.pdf
140.06 Kb -
Hylo®Bond M5101 Activator - German MSDS.pdf
144.87 Kb -
Hylo®Bond M5101 Adhesive - American MSDS.pdf
329.54 Kb -
Hylo®Bond M5101 Adhesive - English MSDS.pdf
307.92 Kb -
Hylo®Bond M5101 Adhesive - German MSDS.pdf
315.72 Kb